ErreLAB offers, as the manufacturer, a complete range of professional level products, from primers to finishes, which are the result of thorough industrial research. This guarantees a complete system for applying resin coatings, having as an aid a sales and support network that covers every technical and application aspect of the product. Not to forget about all the accessories and working tools, indispensable for the state of the art work.

PREPARATION PRIMERS
R101 • CEMENT PRIMER

BICOMPONENT (A+B)

Breathable bicomponent adhesive created with water-based epoxy resins. Suitable for any absorbing surface. May be also used as a transparent impregnating agent to protect concrete floors against oil and dust. Must be always used as an undercoat on cement supports.

 

Mixture/weight ratio: A=600 B=400
Consumption: Variable
Pot-life: 105 min
Colour:

R101_PRIMER_CEMENTO_ErreLab
R102 • TES CEMENT PRIMER

BICOMPONENT (A+B)

Bicomponent epoxy system (A+B) based on epoxy and amine resins in aqueous dispersion. The resulting film has good mechanical properties, a high resistance to solvents and a satisfactory resistance to light.

 

Mixture/weight ratio: A=620 B=380
Consumption: variabile
Pot-life: 120 min
Colour: transparent

R102_PRIMER_CEMENTO_TES_ErreLab
R103 • GS PRIMER

MONOCOMPONENT

 

Mixture/weight ratio: monocomponent
Consumption: 0.075-0.100 kg/m2 per coat
Pot-life: not applicable
Colour:

R103_PRIMER_GS_ErreLab
R104 • LC PRIMER

MONOCOMPONENT

 

Mixture/weight ratio: dilute with water at 1 to 1
Consumption: 0.050-0.150 kg/m2 per coat
Pot-life: not applicable
Colour:

R104_PRIMER_LC
R111 • PRIMER PLUS

BICOMPONENT (A+B)

A bicomponent (A+B) water-based epoxy system. After cross-linking it shows good adhesion on various supports (tiles, concrete and old resin coatings).
As compared to the water-based epoxy systems that exist in the market, it has a shorter Touch Dry time.

 

Mixture/weight ratio: A=570 B=430
Consumption: 0,10 kg/m²
Pot-life: 120 min
Colour:

R111_PRIMER_PLUS_ErreLab
R122 • HS PRIMER

BICOMPONENT (A+B)

Solvent-free, transparent bicomponent (A+B) epoxy compound.
It is based on epoxy resins combined with amine cycloaliphatic hardeners. It has good penetrating and consolidating abilities for cement supports.
The particular chemical structure of the amine hardener guarantees the system’s good reactivity even at low temperatures.

 

Mixture/weight ratio: A=667 B=333
Consumption: .13 kg/m2 variable depending on the use
Pot-life: 30 minutes
Colour: Transparent

R122_PRIMER_HS_ErreLab
R131 • FERRO PRIMER

BICOMPONENT (A+B)
Bicomponent product based on epoxy resins combined with polyamide hardeners.
Due to the high content of solid substances, PRIMER FERRO guarantees a high thickness in just one coat and is an ideal undercoat for applying quartz or iron grains for antiskid coatings.

 

The hardening time and the time before applying a second coat are discreetly short.
Mixture/weight ratio: A=750 B=250
Consumption: 0,25 kg/m²
Pot-life: 20 min
Colour:

R131_PRIMER_FERRO_ErreLab
BASE PASTES
R201 • FONDO WET BASE

THREE COMPONENT (A+B+C)
Three component primer base created with epoxy resins in aqueous dispersion and inorganic binding agents. To be applied with a roller to supports covered with moisture or suffering from capillary infiltration. This product acts as a “vapour barrier”.

 

Mixture/weight ratio: A=390 B=110 C=500
Consumption: 0,25 kg/m²
Pot-life: 45 min
Colour:

R201_FONDO_WET_ErreLab
R202 • FONDO FIBRE BASE

THREE COMPONENT (A+B+C)

Three component primer base created with epoxy resins in aqueous dispersion and inorganic binding agents. To be applied with a steel “American type” trowel as a supporting filling layer. Due to its load of inert aggregates and fibres, it is ideal as means of giving the system a major stability and resistance. Must be always used on tiled floors.

 

Mixture/weight ratio: A=390 B=110 C=500
Consumption: 1 kg/m²
Pot-life: 30 min
Colour:

R202_FONDO_FIBRE_ErreLab
R203 • ERRE-BLOCK BASE

THREE COMPONENT (A+B+C)

Three component compound (A+B+C) based on liquid epoxy resins in aqueous dispersion and hydraulic binding agents, to be used as an undercoat on moist surfaces. Particularly resistant against backdraft humidity.

 

Mixture/weight ratio: A=300 B=200 C=500
Consumption: 0.4-1.0 kg/m2 (per coat)
Pot-life: 90 min
Colour: Dark gray

R203_ERRE_BLOCK_ErreLab
R204 • ERRE-BLOCK ONE BASE

THREE COMPONENT

Three-component formulation (A + B + C) based on liquid epoxy resins in aqueous emulsion and hydraulic binders, used as a primer for floors. Particularly resistant to moisture in counter thrust, it is applicable in a single take

 

Mixture/weight ratio: A=300 B=200 C=500
Consumption: 2-3 kg / m2 for pouring and 0.6-1 kg / m2 for smoothing
Pot-life: at 35 ° C and 50% R.H. 10 minutes, at 25 ° C and 50% R.H. 35 minutes, at 10 ° C and 50% R.H. 60 minutes
Colour: Drak gray

R204-cod
R211 • MALTA MORTAR BASE

THREE COMPONENT (A+B+C)

Three component water-based self-levelling epoxy mortar to be used as an undercoating for the floor. The product forms the bulk of the resin surface. Its consumption varies, depending on the state of the existing support and on the kind of application. Available in white colour.

 

Mixture/weight ratio:  A=220 B=113 C=667
Consumption: variable
Pot-life: 15 min
Colour:

R211_MALTA_ErreLab
R213 • MALTA LEVEL MORTAR BASE

THREE COMPONENT (A+B+C)
Self-levelling mortar composed of epoxy and cement for the floors.

 

Mixture/weight ratio: A=202 B=57 C=741
Consumption: 4.5 kg/m2 per 2.5 mm of thickness
Pot-life: 20 minutes
Colour:

R213_MALTA_LEVEL_ErreLab
R214 • ERRE-LEVEL CEM BASE

MONOCOMPONENT

Ready-made powdered mixture of cements, mineral aggregates, resins and additives. Adding water produces a self-levelling mortar, which can be applied manually or with a pump.

 

Mixture/weight ratio: monocomponent
Consumption: 1.5 kg/m2 per 1 mm of thickness
Pot-life: 30 minutes
Colour:

R214_ERRE_LEVEL_CEM
R215 • MALTA ACCIAIO MORTAR BASE

THREE COMPONENT (A+B+C)
Epoxy mortar reinforced with treated granulated iron, composed of 3 components (A+B+C):
A – amine resin in an aqueous vehicle
B – epoxy resin
C – ready-made mixture of post-treated metal chippings and inorganic additives
The mortar provides coatings with a high mechanical resistance.
The product hardens in the presence o moisture and is highly permeable.

 

Mixture/weight ratio: A=257 B=171 C=572
Consumption: 0.2-1.0 kg/m2 per coat
Pot-life: 15 min
Colour:

R215_MALTA_ACCIAIO_ErreLab
R251 • POWDERED FIBROUS FILLING BASE

MONOCOMPONENT
Monocomponent adhesive filling showing high adhesion ability on various supports.
Specifically good for skim coating and smoothing surfaces in cement plaster or tiles. To be used on vertical surfaces as a levelling undercoat and as an adhesive cushion for the following intermediate layers.

 

Mixture/weight ratio: Monocomponent
Consumption: 1,5 kg/m²
Pot-life: 60 min
Colour:

R251_RIEMPITIVO_FIBRATO_IN_POLVERE
R252 • FINE POWDERED FIBROUS FILLING BASE

MONOCOMPONENT
Thixotropic cement mortar modified with inorganic binding agents, with a great workability and controlled shrinkage.

 

Mixture/weight ratio: Monocomponent
Consumption: 1,5 kg/m²
Pot-life: 60 min
Colour:

R252_RIEMPITIVO_FIBRATO_IN_POLVERE_FINE
R255 • FONDO VERTICAL BASE

MONOCOMPONENT
Monocomponent intermediate base for vertical surfaces, to be used as a levelling undercoat and as an adhesive cushion for the following decorative layers. Available in white colour.

 

Mixture/weight ratio: Monocomponent
Consumption: variable
Pot-life: non applicable
Colour:

R255_FONDO_VERTICAL_ErreLab
DECORATIVE PASTES
R301 • DECORO SPATOLATO GROSSO THICK PASTE

BICOMPONENT (A+B+PIGMENT)

Bicomponent coloured mortar (A+B+Pigment), based on epoxy resins in aqueous dispersion, to be used for skim coating or as a semi self-levelling mortar. It has:
• good adhesive ability on concrete, tiles and resinous coatings
• good adhesion on moist supports and vapour permeability
• good resistance to wear
• it is ideal for applying decorative finishes

 

Mixture/weight ratio: A=850 B=100 Pigment=50
Consumption: Thin skim coating: 0.5-0.8 kg/m2 – Semi self-levelling coating: 2-3 kg/m²
Pot-life: 40 min
Colour: Neutral or White

R301_DECORO_SPATOLATO_GROSSO
R302 • DECORO SPATOLATO PASTE

BICOMPONENT (A+B+PIGMENT)

Two-component mortar created with water-based epoxy resins. Product to be used to obtain SPATULATO (trowelled) and VELATO (veiled) effects. Available as a neutral base, it should be tinted with ColorLAB pastes to obtain the tints shown in the Colour Set folder. Suitable for skim coating in at least 2 hands: for horizontal surfaces thin with water, for vertical surfaces add R842 thickener.

 

Mixture/weight ratio: A=850 B=100 Pigment=50
Consumption: 0.50 kg/m2 (per coat)
Pot-life: 40 min
Colour: Neutro (o Bianco)

R302_DECORO_SPATOLATO
R303 • PIETRA BASE

BICOMPONENT (A+B)

Two component A + B mortar based on epoxy resins in aqueous dispersion, usable for
smoothing or as a workable semi-leveling mortar, it has:
– excellent adhesion on concrete, tiles and resinous coatings
– good wear resistance
– it is ideal for creating decorative effect finishes, in particular all the effects of the line
Pietracontinua
The product is available in two versions: Neutral or Colored (Stone Base 143) depending on the
decorative effects to create.

 

Mixture/weight ratio (Neutral): A=850 B=100 Pigment=50
Mixture/weight ratio (Coloured): A=900 B=100
Consumption:
Low thickness shaving: about 0,5-0,6 kg/m2
Spread coating: 0,8-1,2 kg/m2
Pot-life: 40 min
Colour: Neutral (o Coloured)

R303_BASE PIETRA
R305 • SPATOLATO OUTDOOR

BICOMPONENT (A+B+PIGMENT)

Bicomponent non-yellowing mortar, with a fine grain-size composition, based on polyurethane resins in aqueous dispersion:
– Great adhesion to resinous coatings.
– Great mechanical resistance
– Good resistance to abrasion
– Great resistance to light and atmospheric agents.

Mixture/weight ratio:  A=900 B=50 Pigment=50
Consumption: 0.8 kg/m2 (per 2 coats)
Pot-life: 50 min (at 25°C)
Colour:

R305_SPATOLATO_OUTDOOR
R306 • DECORO CEMENTO PASTE

BICOMPONENT (A+B+PIGMENT)

Bicomponent paste for decorative coatings. A versatile product that gives the surfaces a look of high value. Available as a neutral base, it should be tinted with ColorLAB pastes to obtain the tints shown in the Colour Set folder. Suitable for thin skim coating in 2 hands.
Attention: after stirring with a power drill, wait for 10 minutes to ensure the pre-reaction. After that give the product a second stir-up before applying it.

 

Mixture/weight ratio: A=333 B=647 Pigment=20
Consumption: ca. 350 kg/m2 (per coat)
Colour: White

R306_DECORO_CEMENTO_ErreLab
R307 • LEVEL W MATT PASTE

BICOMPONENT (A+B+PIGMENT)
Bicomponent (A+B) self-levelling epoxy composite in an aqueous emulsion. Composed of an amine resin in an aqueous vehicle (part A) and an epoxy resin in an aqueous emulsion (part B).
Available as a neutral base, it should be tinted with ColorLAB pastes.
The composite allows to create coatings with a high mechanical resistance. It hardens in the presence of humidity and is highly permeable.
The surface is opaque, with fine antiskid grain, easy to clean.

 

Mixture/weight ratio: A=825 B=130 Pigment=45
Pot-life: 30 minutes
Colour:

R307_LEVEL_W_MATT
R308 • LEVEL SF LUX PASTE

BICOMPONENT (A+B+PIGMENT)

Bicomponent compound based on epoxy resins combined with amine cycloaliphatic hardeners. R308 LEVEL SF LUX can be applied with a roller for water-proof and sparkless “antiskid coatings” and “high-thickness painting”. As an alternative, it can be mixed with R825 quartz spheres, to be applied as a “self-levelling coating” or as a “skim-coat system”. Complies with the Legislative decree No 193/2007 “Regulation (EC) No 852/2004 on the hygiene of foodstuffs” (H.A.C.C.P.).

Mixture/weight ratio:  A=750 B=250
Consumption: 2,2 kg/m²
Pot-life: 30 min
Colour:

R308_LEVEL_SF_LUX
R309 • DECORO METALLO PASTE

MONOCOMPONENT
Monocomponent acrylic resin for indoor use, which, due to its special pigments, allows to reproduce METALLO effect on the surface. Available ready-made in tints sampled in the Colour Set folder. May be applied with a roller in 2 coats.

 

Mixture/weight ratio: Monocomponent
Consumption: 0,10 kg/m²
Pot-life: non applicable
Colour:

R309_DECORO_METALLO_ErreLab
R310 • CEMENTO MADRE XL PASTE

MONOCOMPONENT
Monocomponent paste with a gross grain size, based on organic and inorganic binding agents, inert aggregates according to size distribution curve and additives.
The product has the following characteristics:
– good adhesion on tiles
– high mechanical resistance
– good resistance to abrasion
– stable in UV rays
– good water resistance

 

Mixture/weight ratio: Monocomponent – 100 of powder, 25-30 of water
Consumption: 0.8-1.0 kg/m2 (per coat)
Pot-life: 70-100 min (a 25°C)
Colour: White

R310_CEMENTO_MADRE_XL
R311 • CEMENTO MADRE FINE PASTE

MONOCOMPONENT
Monocomponent paste with a fine grain size, based on organic and inorganic binding agents, fillers and additives.
The product has the following characteristics:
– good resistance to abrasion
– stable in UV rays
– good water resistance
Mixture/weight ratio: Monocomponent – 100 of powder, 30-40 of water
Consumption: 0.4 kg/m2 for the 1st coat and < 0.3 g/m2 for 2nd coat.
Pot-life: 70-120 min (at 25°C)
Colour: White

R311_CEMENTO_MADRE_FINE_ErreLab
R312 • ERREFAST XL

MONOCOMPONENT
Ready-to-use single-component skim coat in water dispersion, based on special hydrophobic acrylic resins.
Easy to use, R312 ERRE-FAST XL is particularly suitable for low thickness leveling on any type of substrate, including ceramic, provided that it is properly prepared.
The rheology of the product allows an easy application and the long open time allows ample workability, able to achieve the desired aesthetic effect.
– Good water resistance
– Good breathability
– Good film formation even at medium low temperatures
– Can be colored with suitable water-based pastes

 

Mixture/weight ratio: Ready to use monocomponent
Consumption: 1,0 kg/m2 (varies according to roughness)
Colour: Ivory

R312-cod
R313 • ERREFAST FINE

MONOCOMPONENT

577/5000
Ready-to-use single-component skim coat in water dispersion, based on special hydrophobic acrylic resins.
Easy to use, R313 ERRE-FAST FINE is particularly suitable for the creation of low thickness decorative surfaces applied on R312 ERRE-FAST XL.
The rheology of the product allows easy application; the long open time allows ample workability to achieve the desired aesthetic effect.
– Good water resistance
– Good breathability
– Good film formation even at medium low temperatures
– Can be coloured with suitable water-based pastes

 

Mixture/weight ratio: Ready to use monocomponent
Consumption: 0,5 kg/m2 (varies according to roughness)
Colour: Ivory

R313-cod
COLOURED FINISHES
R405 • VELATURA (VEILED FINISH)

MONOCOMPONENT
Monocomponent polyurethane resin, may be applied with a trowel in thin coats. Must be used to obtain VELATO (veiled) effect. Available ready-made in tints sampled in the Colour Set folder. Available also in colourless, fully transparent version. Suitable for skim coating, must be always covered with a polyurethane aliphatic finish in 1 or 2 coats.

 

Mixture/weight ratio: Monocomponent
Consumption: 0,100 kg/m²
Pot-life: non applicable
Colour: Neutral opalescent or may be chosen from the colour set.

R405 _VELATURA_ErreLab
R411 • EP-COLOR

BICOMPONENT (A+B+PIGMENT)

Two-component finish created with water-based epoxy resins for painting floors and internal walls. Great coloured finish for the general use over resinous coatings. Must be used to obtain MONOCROMO effect. Available as a neutral base, it should be tinted with ColorLAB pastes to obtain the tints shown in the Colour Set folder. May be applied with a roller in at least 2 coats. Before proceeding with the application, make sure to prepare the surface with care. Cover the eventual imperfections with a fast-drying filler, then, when it dries, sand the surface with 120 grain abrasive disks. ATTENTION: always be sure to observe the “INDUCTION TIME”.

 

Mixture/weight ratio: A=640 B=200 Pigment=160
Consumo: 0.080-0.130 kg/m2 per coat
Pot-life: 105 min
Colour: Neutral or White

R411_EP_COLOR_ErreLab
R420 • VELO PIETRA TR

MONOCOMPONENT

Decorative product based on acrylic binding agent and lamellar fillers, created for adding a veil decoration to some of PIETRA CONTINUA effects.
Using particular application techniques (microfibre mop or sponge) allows to create finishes of noticeable chromatic richness.
Available in transparent colouring, it must be thinned with water and tinted with R745 TERRE COLORANTI in proportions, indicated in PIETRA CONTINUA Colour Set folder.

 

Mixture/weight ratio: Monocomponent
Consumption: ca. 0.04 kg/m²
Pot-life: non applicable
Colour: Neutral Opalescent

R420_VELO_PIETRA_TR
R421 • VELO PIETRA

MONOCOMPONENT

Monocomponent water-based acrylic finish, translucent, complemented with special pearly an micaceous pigments.
It allows to create some of PIETRA CONTINUA effects.
Available ready-to-use, tinted according to PIETRA CONTINUA Colour Set samples.
Available in the versions VELOPIETRA KK (anthracite black),
VELOPIETRA Porfido Elegance, Style and Trend (PE, PS, PT) and VELOPIETRA Scisto Elegance, Style and Trend (SE, SS, ST).

 

Mixture/weight ratio: Monocomponent
Consumption: ca. 0.15-0.2 kg/m² in total
Pot-life: non applicable
Colour: Various

R421_VELO PIETRA
R431 • TOP-COLOR

BICOMPONENT (A+B+PIGMENT)
Bicomponent (A+B) coloured polyurethane enamel in an aqueous emulsion.
The product is based on reticulated polyurethane aqueous dispersion with hydrophilic aliphatic polyisocyanate. The film that is produced after the phase of coalescence and cross-linking has the following properties:

  • elevated adhesive ability on various supports
  • great mechanical properties
  • good resistance to abrasion
  • good resistance to solvents
  • great resistance to atmospheric agents
  • good resistance to ethylic alcohol
  • glossy look

Mixture/weight ratio: A=860 B=140
Consumption: 0.100 kg/m2 for a 40 micron thick film
Pot-life: 1 hour
Colour: White

R431_TOP_COLOR_ErreLab
R451 • TOP-COLOR SOL LUCIDO (GLOSSY FINISH)

BICOMPONENT (A+B+PIGMENT)
Bicomponent (A+B) glossy coloured polyurethane enamel based on aliphatic polyurethane resins, contains solvent.
It is resistant to:

• UV rays

• acid rain

• the effect of various acids

R451 TOP-COLOR SOL forms a film that maintains a good flexibility and allows the treatment of metal surfaces.

 

Mixture/weight ratio: A=825 B=175
Consumption: 0,090-0,120 kg/m²
Pot-life: 3 hours
Colour: May be chosen from ErreLab or Ral Colour set folder

R451_TOP_COLOR_SOL_LUCIDO_ErreLab
R452 • • R452 • TOP-COLOR SOL SATINATO (SATIN FINISH)

BICOMPONENT (A+B+PIGMENT)
Bicomponent (A+B) satin coloured polyurethane enamel, based on aliphatic polyurethane resins, contains solvent.
It is resistant to:

• ultraviolet rays

• adic rain

• the effect of various acids

R452 TOP-COLOR SOL SATINATO forms a film that maintains a good flexibility and allows the treatment of metal surfaces.

Mixture/weight ratio:  A=850  B=150
Consumption: 0,090-0,120 kg/m²
Pot-life: 3 hours at 25°C
Colour: May be chosen from ErreLab or Ral Colour set folder

R452_TOP_COLOR_SOL_SATINATO
TRANSPARENT FINISHES
R505 • INTERMEDIO MONO

MONOCOMPONENT

 

Mixture/weight ratio: monocomponent
Consumption: 0,1 kg/m²
Pot-life:
Colour:

R505_INTERMEDIO MONO_MONOCOMPONENTE_ErreLab
R521 • LASTRA

BICOMPONENT (A+B)

Bicomponent (A+B) solvent-free transparent epoxy compound. Reticulated with a cycloaliphatic amine hardener, almost colourless.
Applied as a “self-levelling” coating, LASTRA leaves the underlying layer partly visible. Thus, it is possible to incorporate images and objects.

 

Mixture/weight ratio: A=714 B=286
Consumption: max 2,0 kg/m²
Pot-life: 35 min
Colour: Transparent

R521_LASTRA_ErreLab
R522 • LASTRA SP

BICOMPONENT (A+B)

Bicomponent (A+B) solvent-free transparent epoxy compound. Reticulated with a cycloaliphatic amine hardener, almost colourless.
Applied as a “self-levelling” coating, R522 LASTRA SP leaves the underlying layer partly visible. Thus, it is possible to incorporate images and objects.

 

Mixture/weight ratio: A=625 B=375
Consumption: 1 kg/m2 per 1 mm of thickness (the advised min. thickness is 3 mm)
Pot-life: 35 min
Colour: Transparent

R522_LASTRA_SP_ErreLab
R523 • LASTRA TIX

BICOMPONENT (A+B)

Bicomponent (A+B) solvent-free transparent thixotropic epoxy compound. Reticulated with a cycloaliphatic amine hardener, almost colourless.
Applied as a skim coat, it leaves the underlying layer partly visible, making it possible to incorporate images and decorative effects. Due to the product’s thixotropic properties, it may be also applied as a skim coat to vertical surfaces.

 

Mixture/weight ratio: A=630 B=370
Consumption: 0,35 kg/m²
Pot-life: 30 min
Colour: Transparent

R523_LASTRA_TIX
R531 • TOP-CLEAR LUCIDO (GLOSSY FINISH)

BICOMPONENT (A+B)
Bicomponent transparent finish created with water-based aliphatic polyurethane resins. Glossy version (Gloss 60° = 90). The value varies, depending on the roughness of the surface it is applied to.
This product should be used as the top coat in 1 or 2 hands. If eventually applied in more than 2 hands, it allows to reduce the roughness of certain decorative effects.

 

Mixture/weight ratio: A=820 B=180
Consumption: 0,10 kg/m²
Pot-life: 60 min
Colour:

R531_TOP_CLEAR_LUCIDO_ErreLab
R532 • TOP-CLEAR SATINATO (SATIN FINISH)

BICOMPONENT (A+B)
Bicomponent transparent finish created with water-based aliphatic polyurethane resins. Satin version (Gloss 60° = 30). The value varies, depending on the roughness of the surface it is applied to.
This product should be used as the top coat in 1 or 2 hands. If eventually applied in more than 2 hands, it allows to reduce the roughness of certain decorative effects.

 

Mixture/weight ratio: A=860 B=140
Consumption: 0,10 kg/m²
Pot-life: 120 min
Colour:

R532_TOP_CLEAR_SATINATO_ErreLab
R533 • TOP-CLEAR OPACO (OPAQUE FINISH)

BICOMPONENT (A+B)
Bicomponent transparent finish created with water-based aliphatic polyurethane resins. Opaque version (Gloss 60° = 10). The value varies, depending on the roughness of the surface it is applied to.
This product should be used as the top coat in 1 or 2 hands. If eventually applied in more than 2 hands, it allows to reduce the roughness of certain decorative effects.

 

Mixture/weight ratio: A=860 B=140
Consumption: 0,10 kg/m²
Pot-life: 120 min
Colour:

R533_TOP_CLEAR_OPACO_ErreLab
R551 • TOP-CLEAR SOL LUCIDO (GLOSSY FINISH)

BICOMPONENT (A+B)

Bicomponent (A+B) transparent polyurethane enamel based on aliphatic polyurethane resins, contains solvent.
It is resistant to:
• UV rays
• acid rain
• the effect of various acids
R551 TOP-CLEAR SOL LUCIDO forms a film that maintains a good flexibility and allows the treatment of metal surfaces.

 

Mixture/weight ratio: A=790 B=210
Consumption: 0,100-0,150 kg/m²
Pot-life: 3 hours
Colour:

R551_TOP_CLEAR_SOL_LUCIDO_ErreLab
R552 • TOP-CLEAR SOL SATINATO (SATIN FINISH)

BICOMPONENT (A+B)

Bicomponent (A+B) transparent polyurethane enamel based on aliphatic polyurethane resins, contains solvent as vehicle, silica and opaque wax.

It is resistant to:
• UV rays
• chemical impact of aid rains and corrosive atmosphere
• the effect of various acids
R552 TOP-CLEAR SOL SATINATO forms a film that is quite resistant to abrasion and scratching.

 

Mixture/weight ratio: A=750 B=250
Consumption: 0,120-0,200 kg/m²
Pot-life: 40 min
Colour: Trasparente

R552-cod
R554 • TOP-CLEAR SOL OPACO (OPAQUE FINISH)

BICOMPONENT (A+B)

FBicomponent (A+B) transparent polyurethane finish, based on aliphatic polyurethane resins, contains solvent.
It is resistant to:
• UV rays
• acid rain
• the effect of various acids

 

Mixture/weight ratio: A=800 B=200
Consumption: 0,100-0,150 kg/m²
Pot-life: 40 min
Colour: Trasparente

R554_TOP_CLEAR_SOL_OPACO
TONERS
R731 • COLORLAB TONER

MIXTURE OF PIGMENTS IN AQUEOUS DISPERSION

Toner characterised by its binding agent, composed of a mixture polymeric of moisturisers and dispersing agents.

Compatible with water-based resins in solution, dispersion or emulsion.
ColorLAB Toner R731 Series aqueous dispersions are produced with a high concentration of pigment, a low content of binding agent and a minimum quantity of moisturisers and dispersing agents, which do not alter the properties and the physical and chemical resistance of the resulting paint film.
The total absence of glycols and resins in this series of toners yields eco-compatible final products with a high tolerance level towards a vast range of water-based resins. Indeed, the mix of binding agents used for dispersing and powdering the pigments has been conceived with the double purpose of avoiding the flaking of the pigment and, at the same time, of giving it the maximum possible compatibility with most of the resin compounds that exist on the market.

R731_COLORLAB_TONER
R745 • COLORLAB TERRE NATURALI

“Terre naturali” are mineral clays, oxides and salts, present in nature in various forms. ErreLAB has chosen 20 types of minerals with elegant and valuable tones, which have the chemical compatibility with CEMENTO MADRE system and are ideal for exalting its natural aesthetic and chromatic properties.

R745_COLORLAB_TERRE_NATURALI
UTILITY – ACCESSORIES
R801 • BLINDO MORTAR

BICOMPONENT (A+B)

Bicomponent (A+B) coloured “ant-shrinkage” epoxy mortar. The shipping package includes:
• “A” part – A compound consisting of epoxy resins, inert aggregates containing quartz according to the size distribution curve, pigments and additives
• “B” part – An amine hardener
The mortar, obtained by mixing parts A and B, is paste-like and is not subject to shrinkage and spillage. A rapid increase in resistance to various effects is produced, reaching a great level of mechanical resistance.

 

Mixture/weight ratio: A=925 B=75
Consumption: 5.6 kg/m2 (per 3 mm of thickness)
Pot-life: 20 min
Colour:

R801_BLINDO_ErreLab
R805 • EP-STUCCO

BICOMPONENT (A+B)

Bicomponent (A+B) solvent-free epoxy adhesive filler. The product is based on epoxy resins and amine-polyamide hardeners and has been specifically designed for the ease of use (the 2 components are mixed in equal proportions). It is not subject to shrinkage and does not easily tend to form runs. When hardened, it can be sanded and polished.

 

Mixture/weight ratio: A=560 B=440
Consumption: 1,15 kg/m² 1.15 kg/m2 (per 1 mm of thickness)
Pot-life: 20 min
Colour:

R805_EP-STUCCO_ErreLab
R806 • EP-FLEX

BICOMPONENT (A+B)

Bicomponent transparent elastic product, based on epoxy-polyurethane resins in combination with amine hardeners.
Apart from its role as a consolidating agent in concrete floorings, this system possesses a good elasticity.

 

Mixture/weight ratio: A=780 B=220
Consumption: Variable, depending on the base state
Pot-life: 50-60 minutes
Colour:

R806_EP-FLEX_ErreLab
R811 • SEALANT

MONOCOMPONENT

Monocomponent sealant based on hygro-hardening aromatic polyurethane resins. After cross-linking, it forms an elastic and durable film, which has a great chemical resistance towards water, oil and hydrocarbons. It adheres to various supports: concrete, ceramics, steel sheet, wood, synthetic supports, glass and brass.

Mixture/weight ratio: monocomponent
Consumption:
Pot-life:
Colour:

R811_ SIGILLANTE_ErreLab
R812 • NET GR.65-75

Glass fibre net, grammage 75-100, square cell.

R812_RETINA_GR.65-75_ErreLab
R821 • SMALL GLASS BALLS - 40

Filler for changing the hardness of a surface.

R821_SFERETTE_DI_VETRO_FINI_40_ErreLab
R822 • BIG GLASS BALLS - 150

Filler for changing the hardness of a surface.

R822_SFERETTE_DI_VETRO_GROSSE_150_ErreLab
R823 • WHITE CORUNDUM 220
R825 • QUARTZ SPHERES COVERED IN RESIN
R829 • LAVA SAND
R842 • THICKENER

Thickening material based on fibres and polyethylene.

R842_ADDENSANTE_ErreLab
R843 • UNI SOLVENT

All-purpose diluent and solvent for cleaning tools.

R843_SOLVENTE_UNI_ErreLab
R844 • LIQUID THICKENER
R861 • PEARLY POWDERS
R876 • GLITTER

Synthetic microchips with luminescent effect.

R876_GLITTER_ErreLab
R881 • NEUTRAL CLEANER
R882 • ALCALINE CLEANER
R891 • SPECIAL GLOSSY WAX

Special glossy wax

Consumption: 0,025-0,050 l/m²

R891_CERA_SPECIALE_LUCIDA_ErreLAB
R892 • SPECIAL OPAQUE WAX

Special opaque wax

Consumption: 0,025-0,050 l/m²

R892_CERA_SPECIALE_OPACA_ErreLAB
R981 • TYVEK SHOE COVERS

Cliccando su accetto o continuando a navigare sul sito, accetti l'utilizzo dei cookie da parte nostra. Maggiori informazioni

Questo sito utilizza i cookie per fornire la migliore esperienza di navigazione possibile. Continuando a utilizzare questo sito senza modificare le impostazioni dei cookie o cliccando su "Accetta" permetti il loro utilizzo.

Chiudi